LIQUID-PHASE MIXING LATEX RUBBER SHEET

HOW IS LIQUID-PHASE SPECIAL?
Liquid-phase mixing compound is made with more than 95% superior natural latex.
Unlike other process, It causes minimal damage to microstructure of the finished rubber.
With the result that it provides extremely high strength, resilience and resistance to abrasion, cutting and tearing. It is specifically designed for wet abrasion applications.

L36 Latex Rubber Sheet

PHYSICAL PROPERTY TEST STANDARD VALUES
Hardness Shore A ASTM D2240 36+/-3
Specific Gravity g/cm3 ASTM D397 0.96 +/-0.03
Modulus@500% Mpa ASTM D412 2.1
Tensile Strength Mpa ASTM D412 23 Min
Elongation % ASTM D412 780 Min
Resilience % ASTM D5963 81
Tear Strength N/mm ASTM D624 40 Min
Wet Abrasion 103%
Working Temperature °C -40 – +70